破损水文观测孔涌水封堵技术在高河矿的应用

针对高河矿奥灰水文观测孔空水管锈蚀断裂漏水严重的问题,分析了存在的问题,制定了钻孔涌水封堵技术方案及相应的注浆施工工艺,并进行了为期7天的井下试验。封堵注浆压力达到6 MPa,使用注浆水泥50 t,水泥浆液凝固良好,注浆阀门打开后无出水现象。     

Evaluation of Scale and Corrosion Inhibition of Modified Polyaspartic Acid

Amino acid modified polyaspartic acids were evaluated as calcium-scale inhibitors. Feasibility of scale inhibition experiments was analyzed by molecular dynamics simulation and Gaussian optimization, and the scale inhibition mechanism was theoretically analyzed. Scale inhibition performance was studied by scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, static scale inhibition experiments, and electrochemical performance testing, which provided an experimental basis for the molecular dynamics simulation. The experimental results showed that Arg-SA-PASP has better scale inhibition and corrosion inhibition performance than His-SA-PASP. The scale inhibition effect increased with increasing concentration. Electrochemical tests indicated that Arg-SA-PASP is an excellent scale and corrosion inhibitor.     

汽车安全带固定点失效分析及结构优化

以乘用车后排安全带固定点为对象，基于安全带固定点强度试验结果，通过有限元方法建立模型，简化并调试有限元模型，进行试验对标分析。经过对标后，有限元分析结果与试验结果基本吻合。然后基于对标后的有限元模型对结构进行优化，提高安全带固定点强度，提出优化方案，并通过试验验证，满足法规要求。通过利用CAE分析技术在产品开发过程中的应用，有效找到问题原因并有针对性地加以优化，从而缩短开发周期和节约成本。     

Continuous Flow Fabrication of Block Copolymer–Grafted Silica Micro‐Particles in Environmentally Friendly Water/Ethanol Media

Polymer‐grafted inorganic particles (PGIPs) are attractive building blocks for numerous chemical and material applications. Surface‐initiated controlled radical polymerization (SI‐CRP) is the most feasible method to fabricate PGIPs. However, a conventional in‐batch reaction still suffers from several disadvantages, including time‐consuming purification processes, low grafting efficiency, and possible gelation problems. Herein, a facile method is demonstrated to synthesize block copolymer–grafted inorganic particles, that is, poly(poly(ethylene glycol) methyl ether methacrylate) (PPEGMEMA)‐b‐poly(N‐isopropylacrylamide) (PNIPAM)–grafted silica micro‐particles using continuous flow chemistry in an environmentally friendly aqueous media. Immobilizing the chain transfer agent and subsequent SI‐CRP can be accomplished sequentially in a continuous flow system, avoiding multi‐step purification processes in between. The chain length (MW) of the grafted polymers is tunable by adjusting the flow time or monomer concentration, and the narrower molar mass dispersity (Р< 1.4) of the grafted polymers reveals the uniform polymer chains on the particles. Moreover, compared with the in‐batch reaction at the same condition, the continuous system also suppresses possible gelation problems.     

甘肃某石煤钒矿焙烧灰渣综合利用工艺研究

针对甘肃某石煤钒矿焙烧灰渣综合利用工艺进行研究。浸出过程中,将传统熟化-水浸浸出工艺与中和-酸浸浸出工艺进行对比,综合分析金属收得率及渣率,优选中和-酸浸双级浸出工艺。回收流程经中和酸浸、还原预处理、铝钒共沉、钒液富集等工序逐级分离回收铝、铁、钒等有价金属,并制备工业应用产品高分子比冰晶石、氧化铁红工业颜料并分析产品纯度。此外,对整个工艺流程的产生的废水、废渣进行综合治理。最后,投产经济效益进行了评估分析,为投资建设石煤钒矿焙烧尾渣综合利用项目提供可靠的决策依据。     

Passive micromixer with baffles distributed on both sides of microchannels based on the Koch fractal principle

Since the beginning of the 21st Century, the development of microfluidic chip technology has been very rapid and has attracted the attention of more and more scholars. As an important part of the microfluidic chip, the performance of the micromixer is critical. The fractal structure in the microchannels helps to improve the mixing performance of the micromixer and improve the mixing efficiency of the micromixer. The research results of other scholars are of great significance to the research of the present paper, which mainly studies the effect of changing the baffle state on the mixing efficiency of the micromixer based on the Koch fractal principle. Through simulation analysis, it was found that the mixing efficiency of the baffles distributed on both sides of the microchannel was higher than the mixing efficiency of the baffles distributed on the microchannel side. When the distance between adjacent baffles was divided into 0.15, 0.25 and 0.35 mm, simulated data suggested that the baffle distance of 0.15 mm was best. Increasing the number of baffles from six to eight groups increased the mixing path of the fluid in the microchannel and improved mixing efficiency. A comparison of mixing efficiencies of the 0°, 15° and 30° baffle angles revealed that very significant improvement in mixing efficiency was obtained at 30°. © 2019 Society of Chemical Industry     

离子液体体系卤水提锂的洗涤工艺研究

溶剂萃取法是盐湖提锂的重要工艺方法。采用磷酸三丁酯（TBP）/1-丁基-3-甲基咪唑双三氟甲基磺酰亚胺盐（[C₄mim][NTf₂]）离子液体体系对高镁锂比盐湖卤水中的锂进行萃取分离提取实验,对负载有机相的洗涤和反萃过程进行了研究。萃取实验：在TBP与[C₄mim][NTf₂]体积比为9∶1、相比（有机相与水相的体积比）为2∶1条件下,锂离子与其他离子的分离系数分别为β（锂/钠）=94.70、β（锂/钾）=148.85、β（锂/镁）=131.81。洗涤实验：系统考察了洗涤剂种类及浓度、相比、洗涤次数等因素对杂质离子洗脱率的影响,结果发现氯化锂和盐酸的混合溶液是从负载有机相中洗涤除去杂质离子的有效洗涤剂。洗涤过程适宜条件：洗涤剂中氯化锂浓度为4 mol/L、盐酸浓度为0.5 mol/L,相比为5∶1,洗涤次数为2次。反萃实验：用稀盐酸（1.0 mol/L）对负载有机相进行反萃取,在相比为1∶1条件下,单级反萃率达到97.81%。研究表明,离子液体体系作为一种新型萃取体系,在高镁锂比盐湖卤水中提取锂具有较好的应用前景。     

长走向平行钒铁矿体协同开采方案研究

七角井矿区的钒、铁双层矿体走向长度超4 km且呈近似平行产出，下盘铁矿开采时损失贫化率高且上盘钒矿资源保护难度大。根据钒铁矿体走向长、近平行产出、厚度负相关、空区隐患大的开采技术条件 特征，采用平面分区、开采时序规划、采矿方法优化、区域稳定性控制等技术来实现钒铁矿协同开采。根据铁矿“中间厚、两端薄”、钒矿“中间薄、两端厚”的形态特征，将长走向的钒铁矿体分为东区、中区及西 区。工程空间上，双层矿体共用一套开拓、采准、运输等开采系统；开采时序上，在提高铁矿生产能力的同时保证了钒矿开采的时间灵活性；采矿方法上，东区及西区铁矿采用阶段矿房嗣后膏体微胶结充填法，中区 铁矿采用阶段矿房法转崩落法；此外，通过中区崩落顶板及上盘围岩，东、西区膏体充填方式保证了矿区开采时及开采后的区域稳定性。研究表明：所提出的协同开采方案使矿山铁矿设计开采储量增加了1 064.7万t ，膏体充填每年消耗干抛层、尾矿等矿山固废86万t以上，矿山安全及经济效益明显。